Devcon® 10610 Aluminum Putty, 1 lb, Paste Form, Aluminum, 0.98

Click to enlarge
ITW PERFORMANCE POLYMERS
10610

Devcon® 10610 Aluminum Putty, 1 lb, Paste Form, Aluminum, 0.98

Devcon® 10610 Aluminum Putty, 1 lb, Paste Form, Aluminum, 0.98

Catalog Number:
Manufacturer: ITW PERFORMANCE POLYMERS
Brand: ITW PERFORMANCE POLYMERS
Item ID: DEVC 10610
MPN: 10610
Min Order Qty: 1

Devcon® Aluminum Putty, 1 lb Container, Epoxy Base, Composition: Aluminum flake, Bisphenol A diglycidyl ether resin, Calcium Carbonate, Paste Form, 70 sq-in/lb at 1/4 in Coverage, 2 to 4 hr Drying, 16 hr Curing, Aluminum, Mild Ammonia Odor/Scent, 120 deg Wet/250 deg F Dry, 0.98 Specific Gravity, >200 deg F Flash Point, 8 pH, Applicable Materials: Aluminum, Concrete and Many Other Metals, 2600 psi Tensile Strength

Features

  • Can be machined, drilled or tapped using conventional metalworking tools
  • Fills voids or pores in castings

Specifications

Applicable Materials
Aluminum, Concrete and Many Other Metals
Base Type
Epoxy
Color
Aluminum
Composition
Aluminum flake, Bisphenol A diglycidyl ether resin, Calcium Carbonate
Container Size
1 lb
Coverage
70 sq-in/lb at 1/4 in
Curing Time
16 hr
Drying Time
2 to 4 hr
Flash Point
>200 deg F
Form
Paste
Odor/Scent
Mild Ammonia
Specific Gravity
0.98
Temperature Rating
120 deg Wet/250 deg F Dry
Tensile Strength
2600 psi
pH Range
8

Devcon® Aluminum Putty, 1 lb Container, Epoxy Base, Composition: Aluminum flake, Bisphenol A diglycidyl ether resin, Calcium Carbonate, Paste Form, 70 sq-in/lb at 1/4 in Coverage, 2 to 4 hr Drying, 16 hr Curing, Aluminum, Mild Ammonia Odor/Scent, 120 deg Wet/250 deg F Dry, 0.98 Specific Gravity, >200 deg F Flash Point, 8 pH, Applicable Materials: Aluminum, Concrete and Many Other Metals, 2600 psi Tensile Strength